Structures by: Yanson T. I.
Total: 18
Ca (Cu.83 Al1.27)
Al1.27CaCu0.83
Soviet Physics, Crystallography (= Kristallografiya) (1988) 33, 196-199
a=15.298Å b=15.298Å c=9.289Å
α=90° β=90° γ=120°
Al9CaNi
Al9CaNi
Soviet Physics, Crystallography (= Kristallografiya) (1987) 32, 816-817
a=7.6002Å b=7.6002Å c=7.9457Å
α=90° β=90° γ=120°
Al9Sr5
Al9Sr5
Soviet Physics, Crystallography (= Kristallografiya) (1987) 32, 196-198
a=5.881Å b=5.881Å c=35.71Å
α=90° β=90° γ=120°
Yb1.26 Fe11.21 Ga0.27
Fe11.21Ga0.27Yb1.26
Chemistry - A European Journal (2004) 10, 2972-2976
a=8.5965Å b=8.5965Å c=12.5806Å
α=90° β=90° γ=120°
Yb1.787 Fe17.426
Fe17.426Yb1.787
Chemistry - A European Journal (2004) 10, 2972-2976
a=8.5965Å b=8.5965Å c=8.3871Å
α=90° β=90° γ=120°
Al20Cr2Er
Al20Cr2Er
Izvestiya Akademii Nauk SSSR, Metally (1990) 1990, 202-205
a=14.497Å b=14.497Å c=14.497Å
α=90° β=90° γ=90°
Al20EuV2
Al20EuV2
Izvestiya Akademii Nauk SSSR, Metally (1990) 1990, 199-201
a=14.5809Å b=14.5809Å c=14.5809Å
α=90° β=90° γ=90°
Mn2.99 Al9.677
Al9.677Mn2.99
Acta Crystallographica C (39,1983-) (1995) 51, 792-794
a=14.883Å b=12.447Å c=12.56Å
α=90° β=90° γ=90°
Al10Mn3
Al10Mn3
Acta Crystallographica, Section C: Crystal Structure Communications (1995) 51, 5 792-794
a=14.883(3)Å b=12.447(4)Å c=12.560(3)Å
α=90° β=90° γ=90°
Al2Fe3Si3
Al2Fe3Si3
Acta Crystallographica Section C (1996) 52, 12 2964-2967
a=4.6512(16)Å b=6.3261(24)Å c=7.499(3)Å
α=101.375(23)° β=105.923(17)° γ=101.237(19)°
Al2Fe3Si4
Al2Fe3Si4
Acta Crystallographica Section C (1996) 52, 12 2964-2967
a=3.6687(15)Å b=12.385(7)Å c=10.147(5)Å
α=90.00000° β=90.00000° γ=90.00000°
Al3Si2Y2
Al3Si2Y2
Acta Crystallographica Section C (1994) 50, 9 1377-1379
a=10.220(3)Å b=4.0354(9)Å c=6.617(2)Å
α=90.° β=101.36(3)° γ=90.°
Al41.24Cr5.76Yb6
Al41.24Cr5.76Yb6
Acta Crystallographica Section C (1994) 50, 10 1529-1531
a=10.8670(10)Å b=10.8670(10)Å c=17.554(2)Å
α=90° β=90° γ=120°
Yb Co2 Al8
Al8Co2Yb
Zeitschrift fuer Kristallographie (149,1979-) (1996) 211, 216-216
a=12.383Å b=14.4Å c=3.9608Å
α=90° β=90° γ=90°
Yb4 Ni6 Al23
Al23Ni6Yb4
Zeitschrift fuer Kristallographie - New Crystal Structures (1996) 211, 219-219
a=15.834Å b=4.069Å c=18.18Å
α=90° β=112.84° γ=90°
Tb Fe4.28 Al7.72
Al7.72Fe4.28Tb
Zeitschrift fuer Kristallographie - New Crystal Structures (1997) 212, 505-507
a=8.743Å b=8.743Å c=5.056Å
α=90° β=90° γ=90°
Lu Fe4 Al8
Al8Fe4Lu
Zeitschrift fuer Kristallographie - New Crystal Structures (1997) 212, 505-507
a=8.7256Å b=8.7256Å c=5.0441Å
α=90° β=90° γ=90°
Zr6 Fe Al2
Al2FeZr6
Zeitschrift fuer Kristallographie - New Crystal Structures (1997) 212, 504-504
a=7.9207Å b=7.9207Å c=3.3603Å
α=90° β=90° γ=120°